Qiu Wulin, Luo Shanguo, Luo Yunjun, Tan Huimin, Li Zhengjun, Mai Kancheng, Zeng Hanmin. Effect of Thermal Treatment on the PA-6 in the Blends[J]. JOURNAL OF BEIJING INSTITUTE OF TECHNOLOGY, 1999, 8(2): 124-129.
Citation:
Qiu Wulin, Luo Shanguo, Luo Yunjun, Tan Huimin, Li Zhengjun, Mai Kancheng, Zeng Hanmin. Effect of Thermal Treatment on the PA-6 in the Blends[J].JOURNAL OF BEIJING INSTITUTE OF TECHNOLOGY, 1999, 8(2): 124-129.
Qiu Wulin, Luo Shanguo, Luo Yunjun, Tan Huimin, Li Zhengjun, Mai Kancheng, Zeng Hanmin. Effect of Thermal Treatment on the PA-6 in the Blends[J]. JOURNAL OF BEIJING INSTITUTE OF TECHNOLOGY, 1999, 8(2): 124-129.
Citation:
Qiu Wulin, Luo Shanguo, Luo Yunjun, Tan Huimin, Li Zhengjun, Mai Kancheng, Zeng Hanmin. Effect of Thermal Treatment on the PA-6 in the Blends[J].JOURNAL OF BEIJING INSTITUTE OF TECHNOLOGY, 1999, 8(2): 124-129.
Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods The effects of annealing temperature, annealing time, heating rate, and the step wise annealing were measured by DSC. Results and Conclusion There exists a critical heating rate affecting the middle temperature melting peak. When annealed at the temperature close to the melting peak, the main melting peak of PA 6 shifted to a higher temperature. Within a short time, annealing time has much effect on neat PA 6 but little effect on PA 6 in the blends. Addition of PE results in a decreasing in the height of melting peak. These phenomenon show that the melting behavior of PA 6 was affected by PE, compatibilizer, as well as thermal treatment.